The invention discloses a zirconia filament guide button for silk reeling and a method for preparing the same. The characteristics of a zirconia material of high strength, wearing resistance and self The invention discloses a zirconia filament guide button for silk reeling and a method for preparing the same. The characteristics of a zirconia material of high strength, wearing resistance and selflubrication are utilized, and the injection forming process is adopted; micro pores of which the diameters are between 0.16 and 0.30mm are prefabricated on a biscuit by an ultrasonic puncher; and thelubrication are utilized, and the injection forming process is adopted; micro pores of which the diameters are between 0.16 and 0.30mm are prefabricated on a biscuit by an ultrasonic puncher; and thebiscuit is sintered and formed at a temperature of 1,600 DEG C, and punched with through holes by the ultrasonic puncher so as to prepare the zirconia filament guide button for silk reeling. The technbiscuit is sintered and formed at a temperature of 1,600 DEG C, and punched with through holes by the ultrasonic puncher so as to prepare the zirconia filament guide button for silk reeling. The technical proposal effectively solves the problem of punching micro pores on ceramics and realizes low cost in punching micro pores on ceramics. Compared with the common ceramic filament guide button, theical proposal effectively solves the problem of punching micro pores on ceramics and realizes low cost in punching micro pores on ceramics. Compared with the common ceramic filament guide button, thewear resistance of the zirconia filament guide button is improved by more than ten times, the micro pores are round and uniform, the yarns are smooth, and the grade of raw silk is one grade improved.wear resistance of the zirconia filament guide button is improved by more than ten times, the micro pores are round and uniform, the yarns are smooth, and the grade of raw silk is one grade improved.