The invention relates to a high strength and high wear-resistance zirconium-aluminum-silicon composite self-release glazed ceramic material and a manufacture method thereof, which is characterized inthat the material is prepared by the following raw materials according to the following steps: the raw materials are calcined polishing aluminum oxide, zirconium silicate, yttria, cerium oxide, magnesium oxide, calcium carbonate and titanium oxide; the steps are as follows: putting the raw material into a ball grinder, adding water, and adding polyving akohol with 5% concentration to carry out wet-ball milling to obtain sizing agent; and then atomizing and drying sizing agent to obtain dry mash which is molded by isostatic pressing to obtain green-ware; sintering the green-ware in a reducing atmosphere by adopting a high-temperature drawer kiln to obtain the high strength and high wear-resistance zirconium-aluminum-silicon composite self-release glazed ceramic material. Compared with aluminum oxide ceramic material, the zirconium-aluminum-silicon composite self-release glazed ceramic material has high strength, high tenacity and high wear-resistance; the production technique is simpleand the sintering temperature is reduced by a wide margin, thus achieving the purpose of energy-saving and consumption reducing.