The invention discloses a lithium battery anode material and a manufacturing method thereof. The anode material comprises the following materials: 100 grams of acetylene black, 800 milliliters of anhydrous ethanol, 8 grams of electrolytic copper powder, 8 grams of polytetrafluoroethylene emulsion and 0.1 gram of H1 additive. The manufacturing method comprises the following steps: weighing the required materials; dissolving H1 into the anhydrous ethanol; dissolving the polytetrafluoroethylene emulsion into the anhydrous ethanol; pouring the acetylene black and the anhydrous ethanol solution into a stirrer and stirring the solution for 4 to 6 minutes; uniformly adding the electrolytic copper powder into the solution by using a screen; stirring the solution for 9 to 11 minutes; repeating the steps to mix a pot of material in which the total amount of the acetylene black is 1,500 grams, and weighing the rest materials according to a proportion; after each pot of materials is mixed, and manually kneading the mixture thrice for 10 minutes each time by using a plastic basin or/and a stainless steel basin; and drying the mixture under vacuum, and fibrillating the mixture. The method has the advantages of low cost and higher safety, and is favorable for production operation.