The invention relates to a production method of glazed ceramic board members, which comprises the following steps: 1) weighing the following raw materials in part by weight: 60-75 parts of AiO2, 16-28 parts of AL2O3, 0-3 parts of Fe2O3, 0-3 parts of TiO2, 0-5 parts of CaO, 0-5 pars of MgO and 0-8 parts of KNa, mixing and adding into a ball mill, and adding 30-38 parts of water by weight for ball milling; 2) screening through a screen till the weight is less than 10 percent of total weight of a mixture; 3) drying the mixture screened in the step 2) through a spray drying tower; 4) agitating the mixture obtained in the step 3) and then adding water till the moisture content is 14-18 percent; 5) pelleting an ingredient obtained in the step 4) through the screen, and forming and extruding through a vacuum extruder to obtain a ceramic board member blank body; 6) drying; and 7) glazing, connecting glazed ceramic board members in series by using a high-temperature roll from an inner hole, putting the ceramic board members onto kiln furniture in a suspending manner and putting into a roll kiln for calcining. The production method has the beneficial effects that a glazed surface is prevented from being bonded with a high-temperature cushion plate after the glazed ceramic board members are sintered, and the effect is remarkable.