The invention discloses an aqueous acrylic acid based anticorrosive static conductive paint and a preparation method thereof. The preparation method comprises the steps: firstly, adding emulsion, a dispersant, a wetting agent, a flash-rust inhibitor, a coupling agent, a defoaming agent and water into a slurrying tank, and dispersing at a high speed, wherein the emulsion, the dispersant, the wetting agent, the flash-rust inhibitor, the coupling agent and the defoaming agent are weighed according to formula quantity, and the added water is 50-80% of water in the formula quantity; adding ferrotitanium powder, titanium dioxide, talcum powder, calcium carbonate, a precipitation inhibitor, and graphite, dispersing at high speed continuously, and then, pumping the dispersed materials into a sanding tank through a vacuum pump; and pumping sanded suspension into a paint mixing tank through the vacuum pump, adding a thickening leveling agent and a coalescing agent, regulating viscosity by using the residual water, then sieving and subpackaging. Compared with a solvent type anticorrosive static conductive paint, the anticorrosive static conductive paint disclosed by the invention has excellent resistance to acid, alkali, salt, water and oil because the adopted emulsion, pigments, function fillers and aids are all nontoxic environment-friendly products, and the surface resistance of an obtained coating can be regulated between 105 omega and 1011omega as required.