The invention provides an andalusite-SiC-C brick for the liquid iron zone of a torpedo car and a method for producing the same. The product has the advantages of excellent resistance to heat shocks, resistance to oxidation, resistance to liquid iron and liquid iron pretreatment erosion and the like. The raw materials of the andalusite-SiC-C brick provided by the invention include 30-80wt% of andalusite, 5-15wt% of alumina micro powder, 5-22% of silicon carbide and nitride, 1-4wt% of plastic-phase metal single element and antioxidant, 5-15wt% of flaky graphite and 3-5wt% of applied liquid phenolic resin by weight. The raw materials are subjected to dosing, mixing, molding and strict roasting at the highest roasting temperature in the range of 180 to 250 DEG C, so that the andalusite-SiC-C brick having excellent properties for the torpedo car is obtained. According to the invention, the andalusite is used in stead of adamantine spar and compact bauxite in the present ASC refractory material; and in addition, the plastic-phase metal single element is added and the strict roasting control rule is employed, so that the damage on the refractory material caused by high-temperature fluctuation between tapping iron and receiving iron in the use process of the torpedo car at present is avoided and the heat of the torpedo car can be obviously improved.