The invention discloses a cold rolling plate for single layer Bundy tube, which contains: 0.0010-0.0060 wt% of C, no more than 0.02 wt% of Si, no more than 0.30% of Mn, less than 0.020 wt%, 0.020-0.060 wt% of Al, no more than 0.0050 wt% of N, less than 0.1 wt%, and the balance being Fe. The invention also discloses a production method, which includes the steps in sequence: hot rolling, cold rolling and hot galvanizing; the hot rolling includes: heating a casting blank to 1100-1200 DEG C, and controlling the finishing temperature in the range of 840-900 DEG C and the reeling temperature in the range of 580-700 DEG C. The cold rolling plate for single layer Bundy tube provided by the invention achieves economic and stable production of the cold rolling plates for single layer Bundy tube in batch by designed chemical components and production technology system.