CN103641461A 一种耐磨陶瓷涂料及其制备方法 无效 - 撤回

一种耐磨陶瓷涂料及其制备方法
摘要：
本发明涉及一种耐磨陶瓷涂料及其制备方法，属于陶瓷技术领域，其中各组分的重量份为石英25~35份、电熔刚玉30~40份、莫来石3~8份、铝酸盐水泥5~10份，其制备方法是将上述各组分混合搅拌均匀，在1500~1550℃的高温融化1.5~2.0小时，干燥即得耐磨陶瓷涂料；该耐磨陶瓷涂料由于石英的加入，大大提高其力学性能，其抗折强度及耐压强度更是超过了金属材料，使得样品的耐磨性能提高。
摘要（英）：

The invention relates to a wear-resistant ceramic coating material and a preparation method thereof, belonging to the technical field of ceramics. The wear-resistant ceramic coating material contains the following ingredients in parts by weight: 25-35 parts of quartz, 30-40 parts of electro-melting corundum, 3-8 parts of mullite and 5-10 parts of aluminate cement. The method comprises the steps of uniformly mixing and stirring all the ingredients, melting for 1.5-2.0 hours at the high temperature of 1,500-1,550 DEG C, and drying, thereby obtaining the wear-resistant ceramic coating material. According to the wear-resistant ceramic coating material, due to the addition of quartz, the mechanical properties are improved greatly, and the flexural strength and compressive strength are higher than those of metallic materials, so that the wear resistance of samples is improved.

0/0