The invention discloses a production method for a double-zero aluminum foil. The production method includes subjecting an aluminum-alloy molten mass to cast rolling to produce a cast rolling coil with the thickness of 6.5-8.0mm after degassing and deslagging, subjecting the cast rolling coil to first cold rolling to produce an aluminum coil with the thickness of 2.0-3.0mm, performing first heat treatment on the aluminum coil subjected to the first cold rolling at the temperature of 450-550 DEG C for 15-20 hours, subjecting the aluminum coil subjected to the first heat treatment to second cold rolling to produce an aluminum coil with the thickness of 0.6-0.8mm, and performing second heat treatment on the aluminum coil subjected to the second cold rolling at the temperature of 300-380 DEG C for 6-12 hours; subjecting the aluminum coil subjected to the second heat treatment to third cold rolling to produce an aluminum coil with the thickness of 0.05-0.1mm, heating the aluminum coil to the aluminum-foil recrystallization critical temperature of 250-310 DEG C, keeping the aluminum coil at the temperature for 5-10 hours, and subjecting an aluminum foil to fourth cold rolling to produce the double-zero aluminum foil with the thickness of 0.006-0.009mm. The double-zero aluminum foil produced by the production method has tensile strength of more than 95Mpa, ductility of more than 3.1%, small blank grain size, few surface stripes, few needle holes and stable quality.