The invention relates to a production method for a cold-rolled steel sheet with an excellent stamping property. The production method comprises the following steps: controlling the ingredients of molten steel; casting a steel blank from the molten steel; heating; roughly rolling; precisely rolling; coiling; carrying out cold rolling; continuously annealing, wherein a temperature in a heating section is 780-810 DEG C, a temperature in a soaking section is 820-850 DEG C, a temperature in a slow cooling section is 670-700 DEG C, a temperature in a rapid cooling section is 440-470 DEG C, and a temperature in an overaging section is 400-430 DEG C, and cooling to a room temperature. According to the production method disclosed by the invention, the performances of the product achieve the following requirements: a yield strength of 120-150MPa, a tensile strength of 280-320MPa, an elongation rate of not less than 45.0%, a plastic strain ratio of not less than 3.0 and a strain hardening index of not less than 0.25; the product has a quite low yield ratio, high elongation rate and plastic strain ratio, and great stamping moulding machining property.