The invention relates to a process for the preparation of polypropylene having - a molecular weight by weight of 450,000-950,000, - a molecular weight distribution of 3-6, - a melt flow in the range of 7-14 dg/min measured with a load of 21.6 kg at 230 DEG C or 0.05-2 dg/min measured with a load of 2.16 kg at 230 DEG C and - xylene soluble content of 2-6 wt% by converting propylene into the polypropylene without pre-polymerization in the presence of a polymerization catalyst under a condition where the volume ratio of H2 to propylene is at most 0.0020, wherein the catalyst comprises a catalyst component and a co-catalyst, wherein the catalyst component is obtained by a process wherein a compound with formula Mg(OAIk)xCly wherein x is larger than 0 and smaller than 2, y equals 2-x and each Alk, independently, represents an alkyl group, is contacted with a titanium tetraalkoxide and/or an alcohol in the presence of an inert dispersant to give an intermediate reaction product and wherein the intermediate reaction product is contacted with titanium tetrachloride in the presence of an internal donor.