There is provided a packaging film that is free from occurrence of blocking upon storage, and deterioration in adhesion to containers even when used under low-temperature conditions, notwithstanding the film is produced while effectively utilizing exhaustible resources. A wrap film of the present invention comprises a laminated film constituted of at least three layers including opposite surface layers comprising a plant-derived polyethylene resin, in which the wrap film has a storage elastic modulus (E') at 20°C of 100 MPa to 4 GPa and an average loss tangent (tan´) at -40 to 0°C of not less than 0.08 as measured at an oscillation frequency of 10 Hz and a distortion of 0.1% by a dynamic viscoelasticity measuring method described in the Method A of JIS K 7198.