CN105153223B 一种用于3D打印的SLA型含磷丙烯酸酯预聚物及其制备方法 有权

一种用于3D打印的SLA型含磷丙烯酸酯预聚物及其制备方法
摘要：
本发明公开了一种用于3D打印的SLA型含磷丙烯酸酯预聚物及其制备方法，其制备方法步骤为：将2‑甲基‑2，5‑二氧‑1，2‑氧磷杂环戊烷OP与羟基丙烯酸酯类化合物以摩尔比1:1的比例混合，加入催化剂和阻聚剂在110‑130℃下反应5‑6h，得到含磷丙烯酸酯预聚物，含磷丙烯酸酯预聚物其结构通式为：其中，R1＝H2C＝CH‑或R2＝‑CH2‑CH2‑、或‑CH2‑CH2‑CH2‑CH2‑中的一种。
摘要（英）：

The invention discloses a SLA type phosphorus-containing acrylic acid ester prepolymer for 3D printing and a preparation method thereof, and the preparation method comprises the following steps: mixing 2-methy-2,5-dioxo-1,2-oxaphospholane OP and hydroxyl acrylate compounds according to a mol ratio which is 1:1, adding a catalyst and a polymerization inhibitor, carrying out a reaction at 110-130 DEG C for 5-6 hours, and obtaining the phosphorus-containing acrylic acid ester prepolymer, and the structure general formula of the phosphorus-containing acrylic acid ester prepolymer is shown in the figure, wherein R1 = H2C = CH- or R2 = -CH2-CH2- or -CH2-CH2-CH2-CH2-.