The invention relates to an anti-reflection dip coating type ramie textile fabric. The outer surface of ramie base cloth is decorated with a layer of functional coating by dip coating; and the coating slurry of the functional coating is prepared by the following steps: adding a coating adhesive, silane, a delustering agent and a cross-linking agent into a slurrying tank; stirring uniformly; adjusting the pH to 7.5-8.5 using ammonia water; standing for 2-4 hours; applying the product to the surface of the ramie base cloth by dip coating; drying for 0.5 hour at 80 DEG C; curing for 1-1.5 hours at 120-135 DEG C; and finally, balancing for more than or equal to 8 hours in natural conditions. After the surface of the ramie textile fabric is protected by the coating material, the textile has better anti-reflection characteristic, and the using quality of the fabric is improved.