The invention relates to a gold oil droplet glazing method for red stoneware. The method includes the following steps that red stoneware clay is poured through a reverse pouring method, a blank is obtained through demolding and is dried in the shade until the water content is 8-10%; the blank is put into a kiln for biscuiting, before reaching 500 DEG C, the temperature is raised at the speed of 1.5 DEG C/min until the temperature reaches 700-800 DEG C, and the blank is continuously fired for 2-3 h and then taken out of the kiln; middle layer glaze is applied to the surface of red stoneware clay biscuiting blank, the blank is put into the kiln for firing after being dried in the shade and is fired for 6-7 h at the temperature of 1000-1100 DEG C, and after the temperature is kept for 30 min, the blank is cooled to 200-250 DEG C and then is taken out of the kiln; gold oil droplets are sprayed to the surface of the cooled middle layer glaze for glazing, the thickness of the glaze slip coating is 0.3-1.5 mm, then the coating is dried at the temperature of 60 DEG C, the blank is put into the kiln after the coating is dried and is fired at the temperature of 1000-1120 DEG C, incomplete combustion timber is put into the kiln to serve as reducing atmosphere, the temperature is kept for 2-3 h, and then the blank is put into a room with the room temperature of 20-25 DEG C to be naturally cooled to obtain the finished product.