The invention discloses an antistatic flame-retardant EVA/PVC composite foamed material, which is prepared from the following raw materials in parts by weight: 100 parts of EVA, 50 to 100 parts of PVC, 10 to 30 parts of compatilizer, 10 to 30 parts of flexibilizer, 20 to 30 parts of fire retardant, 30 to 50 parts of plasticizer, 6 to 10 parts of foaming agent, 0.5 to 2 parts of crosslinking agent, 0 to 2.5 parts of surface treating agent, 10 to 40 parts of antistatic agent, and 1 to 10 parts of other auxiliary agents. The obtained EVA/PVC composite foamed material has the characteristics of good resilience, high tensile strength and tearing strength, large breaking elongation rate, bending resistant property, low density, and small compression deformation amount, is flame-retardant and antistatic, and can be applied to the fields of electronic package and fire fighting.