The invention relates to a rolling process for improving electric conductivity and strength of an aluminum lead. After a flat aluminum blank is formed by pouring, the rod rolling treatment and the annealing treatment are performed; the rod rolling treatment is to perform primary rolling and final rolling in a rolling machine; the temperature of entering the rolling machine is not higher than 150 DEG C; the temperature is not higher than 150 DEG C after primary rolling; the temperature is 150-190 DEG C after final rolling; and the annealing treatment is to keep the temperature of 150-190 DEG C by 8-10 h. The rolling process can effectively improve the electric conductivity of the lead, reduces the power transmission energy consumption, improves the production pass percent when guaranteeing the electric conductivity and the strength, reduces the production cost of the aluminum lead, and is better in economic benefit and social benefit.