The invention relates to a preparing method for a VC high alloy cold work die steel base steel bond hard alloy. The preparing method includes the following steps that titanium carbide powder and high alloy powder cold work die steel matrix powder are weighed according to the proportion, alloy powder is put into a ball grinding machine to be mixed and smashed, added absolute ethyl alcohol is a process control agent, and the wet mixed powder is put into a vacuum drying box to be dried after ball grinding and is used for standby use after drying; an organic monomer and an initiator are added into a solvent to prepare pre-mixed liquid; an additive improving slurry fluidity and dispersity is added; a catalyst and a pH modifier are added and are evenly stirred, and slurry is obtained; and the slurry is injected into an injection and coagulation die, vacuum suction or vibration gas removing is conducted, after the slurry is cured to be formed, a blank is put into the vacuum drying box to be dried, the dried blank is subjected to integrated degumming and sintering in a vacuum sintering furnace, and the steel bond hard alloy is prepared. The preparing method has the beneficial effects that the technology is simple, the cost is relatively low, and parts large in size and complex in shape are easy to prepare on the basis that the macro performance of the steel bond hard alloy is ensured.