The invention discloses a quick-curing acrylate pressure-sensitive adhesive. The quick-curing acrylate pressure-sensitive adhesive is prepared from the following raw materials in parts by weight: 70-85 parts of viscous monomer, 0-25 parts of cohesion monomer, 1-10 parts of functional monomer, 0.3-0.8 part of free-radical polymerization initiator, 100-150 parts of solvent, 5-10 parts of curing monomer and photosensitizer accounting for 1-3% of the curing monomer in weight, wherein the curing monomer is at least one of trimethylolpropane triacrylate, tris(2-hydroxyethyl)isocyanurate triacrylate and pentaerythritol triacrylate. According to the invention, the multifunctional curing monomer is used to from a mutual transmission network structure between molecular chains under a UV (ultraviolet) condition so as to cure the pressure-sensitive adhesive, thereby obviously shortening the curing time; no adhesive residue phenomenon exists under the condition of normal use and treatment; the adhesive has strong adhesive force and high release force; and no adhesive failure and adhesive layer and interface damage phenomena exist in the use process. Thus, the quick-curing acrylate pressure-sensitive adhesive has great application value and market value.