The invention relates to a shock absorber guiding device and belongs to the technical field of powder metallurgy. The shock absorber guiding device comprises the following components including, by weight, 1-3 parts of graphite powder, 20-40 parts of copper powder, 3-8 parts of manganese sulfide powder, 1-5 parts of nickel powder, 0.01-0.08 part of Bi2(SO4)3 powder, 1-5 parts of boron carbide, 1-5 parts of zinc stearate and 40-80 parts of iron powder. By means of the shock absorber guiding device, due to the fact that raw materials of the shock absorber guiding device are reasonable matched, a protection agent is sprayed during secondary pressing forming and secondary pressing and shaping is conducted under large pressure, the shock absorber guiding device can have extremely good strength, hardness and wear resistance, the density of the manufactured guiding device is larger than 6.7 g/cm<3>, the surface hardness is larger than 90 HB, the strength is larger than 700 MPa, cleanliness reaches the 8th level, and therefore the service life of the shock absorber guiding device is greatly prolonged.