The invention relates to a novel aluminum corrosive foil pre-treatment process which comprises the following steps of: (1) putting an aluminum plain foil in a pre-treatment liquid to be soaked for 45s; (2) then cleaning the foil thoroughly, putting the foil in a primary corrosive mixed liquid at 70 DEG C, and applying a direct current, the current density of which is 0.70A/cm<2> for electrolytic corrosion for 60s; (3) cleaning the foil thoroughly with pure water, putting the foil in a tank liquid containing 2% of nitric acid at 70 DEG C, and applying a direct current, the current density of which is 0.15A/cm<2> for electrolytic corrosion for 600s; and (4) finally, cleaning the foil thoroughly with pure water, and then putting the foil in an oven at 220 DEG C to be dried. The process provided by the invention overcomes related defects that the corrosive foil which is pre-treated is likely to deform, the surface of the foil is of chromatic aberration after treatment, trace elements beneficial for generating holes will be removed through treatment, follow-up operations are not facilitated and the like.