CN107721235A 一种陶瓷研磨体专用水泥助磨剂及其制备方法 无效 - 驳回

一种陶瓷研磨体专用水泥助磨剂及其制备方法
摘要：
本发明公开了一种陶瓷研磨体专用水泥助磨剂及其制备方法，该助磨剂由聚乙二醇10％-20％、丙三醇5％-25％、十六烷醇5％-10％、蜜糖6％-10％、三乙醇胺3％-12％，余量为水；陶瓷研磨体专用水泥助磨剂的制备方法，包括以下步骤：将组分的有效成份和蒸馏水投入在反应釜中，反应釜保持常压，温度控制在20-40℃，搅拌速度控制在15-25r/min，持续搅拌1-2h，即可得到本产品。该可以良好地应用于陶瓷研磨体，且该产品配方简单，生产工艺简单，有益于大批量生产。
摘要（英）：

The invention discloses a special cement grinding aid for a ceramic grinding body and a preparation method of the special cement grinding aid. The special cement grinding aid is prepared from the following components: 10-20 percent of polyethylene glycol, 5-25 percent of glycerol, 5-10 percent of cetyl alcohol, 6-10 percent of gooey, 3-12 percent of triethanolamine and the balance of water. The preparation method of the special cement grinding aid for the ceramic grinding body comprises the following steps of pouring effective compositions of the components and distilled water in a reaction kettle, enabling the reaction kettle to keep normal pressure, controlling a temperature at 20-40 DEG C and a stirring speed at 15-25r/min, and continuously stirring for 1-2h to obtain the product. The special cement grinding aid can be well applied to the ceramic grinding body, is simple in formula and production process and is beneficial to mass production.

0/0