CN1085198A 一种硅镁合成陶瓷瓦的生产方法 无效 - 撤回

一种硅镁合成陶瓷瓦的生产方法
摘要：
本发明涉及一种含硅镁为主要原料的合成陶瓷瓦的生产方法。该方法是将按一定的比例组成的配料和配液搅拌混合均匀后的浆料存放六小时，在瓦模上置一平板先铺上一层聚酯膜，将浆料铺成1.5mm厚，抹平。放一层玻璃丝布，再加2mm厚的浆料抹平，再放一层玻璃丝布之后加1.5mm厚浆料，铺平、抽出平板落入瓦模内固化六小时脱模，养护15天，表面再涂一层防水剂二甲基硅油即最终产品，按该方法制成的合成陶瓷瓦，具有成本低，性能好，寿命长，适合大量推广应用。
摘要（英）：

Synthetic Si-Mg porcelain tile is made up through preparing slurry from raw materials, standing for 6 hours, putting a flat plate on tile mould, spreading a polyester film, spreading slurry with 1.5 mm thickness, laying a layer of glass fibre cloth, spreading slurry with 2mm thickness, laying a layer of glass fibre cloth, spreading slurry with 1.5mm thickness, drawing flat plate out to make raw material drop into mould, solidification for 6 hours, demoulding, curing for 15 days, and coating water-proofing agent (dimethyl silicone oil). It features low cost, high performance and long service life.