The invention relates to a ceramic green body containing flue gas desulfurization waste residue and a production method of the ceramic green body. The ceramic green body comprises the following components in parts by weight: 32 parts of clay, 47 parts of sand, 8 parts of limestone, 11 parts of wollastonite, 2 parts of waste ceramic powder, 2 parts of desulfurization waste residues, 0.1 part of a hexamer, 0.1 part of sodium silicate pentahydrate, 0.85 part of water glass and 0.05 part of sodium naphthalene sulfonate. The method comprises the following steps: (1) weighing the desulfurization waste residues, then mixing the raw materials with ballstone and water according to a ratio of 1:1.2:0.50, and carrying out ball milling and aging to obtain desulfurization waste residue glaze slurry; (2) weighing a conventional ceramic green body according to the formula weight, feeding the raw material, ballstone and water into a ball mill according to a ratio of 1:1.2:0.44, carrying out ball milling, and carrying out aging to obtain ceramic green body glaze slurry; (3) discharging the desulfurization waste residue glaze slurry and the ceramic green body glaze slurry from slurry tanks, pumpingthe desulfurization waste residue glaze slurry and the ceramic green body glaze slurry into a transfer slurry tank for mixing according to a ratio of 2:100, feeding the mixture into a spray tower through a suction pump hose, and carrying out spray granulation to obtain green body powder particles; and (4) placing the granular powder into a material bin for aging, sending the aged granular powder into a press die cavity through a belt, and carrying out pressing forming to obtain the flue gas desulfurization waste residue-containing ceramic green body.