The present disclosure provides a process. The process includes (i) melt blending, in an extruder, (a) a polyolefin phase and (b) an aqueous phase in the presence of (c) at least one dispersant selected from an acrylic dispersant, a poloxamer dispersant, and combinations thereof; (ii) producing an interfacial tension from 0.1 dynes/cm to 25 dynes/cm; (iii) forming a polyolefin aqueous dispersion having from 25 wt% to 90 wt% solids content of dispersion; and (iv) removing the water from the polyolefin aqueous dispersion to form a powder. The powder has a mean volume average particle size from 10 [mu]m to 300 [mu]m, a sphericity from 0.92 to 1.0, a particle size distribution from 1 to less than 2, and a particle density from 98% to 100%.