Porous bodies are produced which are suitable for use as supports for catalysts, including living cells, such as bacteria. The bodies have a significantly large average pore diameter of about 0.5 to 100 microns, (i.e. 5,000 to 1,000,000 Å) and a total pore volume of about 0.1 to 1.5 cc/g with the large pores contributing a pore volume of from about 0.1 to 1.0 cc/g. The bodies are made by preparing a mixture of ultimate particles of bound clay, one or more optional ingredients such as inorganic binders, extrusion or forming aids, burnout agents, or a forming liquid, such as water. In a preferred embodiment, the ultimate particles are formed by spray drying.
The porous bodies with bacteria or microorganisms supported thereon are used as biocatalysts for the decontamination of aqueous waste streams or contaminated vapors.