Disclosed is a process for obtaining polyester articles, including foamed articles, containing low levels of extractable branching agent. The process comprises: (1) forming a molten mixture comprising (i) a major amount of a first resin composition comprising polyester and from 0 up to about 1 wt. % of a compound capable of branching the polyester, and (ii) a minor amount of a second polyester resin composition comprising at least about 50 wt. % polyester resin and greater than about 2 wt. % of a compound capable of branching the polyester, wherein the relative amounts of (i) and (ii) are such that said molten mixture comprises from about 0.1 wt. % to about 1 wt. % of said branching compound; (2) adding a blowing agent to the molten mixture; and (3) extruding the resultant mixture to obtain a foam. The invention is also directed to the second composition used in the above process, and foamed polyester articles obtained from the process.