A propylene polymer composition comprising (percent by weight): A) 74%-84% of a propylene homopolymer having a Polydispersity Index (P.I.) value of from 4.6 to 10, a fraction insoluble in xylene at 25 °C, higher than 90 %, and a MFR L (Melt Flow Rate according to ISO 1133, condition L, i.e. 230°C and 2.16 kg load) from 110 to 200 g/10 min; B) 16%-26%, of a copolymer of propylene with from 39% to 48%, of ethylene derived units; the composition having an intrinsic viscosity of the fraction soluble in xylene at 25 °C comprised between 2.7 and 4.0 dl/g; and a MFR L (Melt Flow Rate according to ISO 1133, condition L, i.e. 230°C and 2.16 kg load) from 30 to 80 g/10 min.