Heat-resistant alloy for production of aerosol cans from a material having the following contents of alloying additions in percent by weight:
according to the standards EN 573-3
EN AW 1050A
Si ≤ 0.25; Fe ≤ 0.40; Cu ≤ 0.05; Mn ≤ 0.05; Mg ≤ 0.05; Zn ≤ 0.07; Ti ≤ 0,05;
EN AW 3102
Si ≤ 0.40; Fe ≤ 0.70; Cu ≤ 0.10; Mn 0.05-0.40; Zn ≤ 0.30; Ti ≤ 0.10;
EN AW 3207
Si ≤ 0.30; Fe ≤ 0.45; Cu ≤ 0.10; Mn 0.40-0.80; Mg ≤ 0.10; Zn ≤ 0.10;
or with more specific compositions
- Si = 0.05÷0.09; Fe = 0.15÷0.27; Cu ≤ 0.005; Mn ≤ 0.005; Mg ≤ 0.005; Zn ≤ 0.015; Ti = 0.01÷0.03;
- Si = 0.05÷0.09; Fe = 0.23÷0.27; Cu ≤ 0.005; Mn = 0.28÷0.32; Mg ≤ 0.005; Zn ≤ 0.015; Ti = 0.01÷0.03;
- Si = 0.05÷0.09; Fe = 0.23÷0.27; Cu ≤ 0.005; Mn = 0.58÷0.62; Mg ≤ 0.005; Zn ≤ 0.015; Ti = 0.01÷0.03;

where each composition contains added Zr in the amount ranging between 0.05 and 0.20% by weight, the sum of the contained amounts of all the secondary elements being ≤ 0,10% by weight and Al content is remainder.