Disclosed is a high-strength steel sheet having a tensile strength (TS) of 780 MPa or more and excellent in ductility, fatigue properties, stretch flangeability, surface characteristics, and sheet passage ability that can be obtained by providing a predetermined chemical composition and a steel microstructure that contains, by area, 20-50 % of ferrite, 5-25 % of bainitic ferrite, 1-10 % of martensite, and 5-15 % of tempered martensite, and that contains, by volume, 10 % or more of retained austenite, in which the retained austenite has a mean grain size of 2 µm or less, a mean Mn content in the retained austenite in mass% is at least 1.2 times the Mn content in the steel sheet in mass%, the retained austenite has a mean free path of 1.2 µm or less, and the tempered martensite has a mean free path of 1.2 µm or less.