A method for manufacturing a grain-oriented electrical steel sheet includes: a silicon steel material production process of producing a silicon steel material; a hot rolling process of obtaining a hot rolled sheet by subjecting the silicon steel material to hot rolling; a cold rolling process of obtaining a steel sheet of a final sheet thickness by subjecting the hot rolled sheet to a single cold rolling process or multiple cold rolling processes having intermediate annealing performed between the cold rolling processes; a decarburization annealing process of subjecting the steel sheet to decarburization annealing; and a final annealing process of applying an annealing separator containing alumina as a main component to the steel sheet and subjecting the steel sheet to final annealing. The silicon steel material contains: in terms of mass%, Si: 0.8 to 7.0%; C: 0.085% or less; acid-soluble Al: 0.010 to 0.065%; N: 0.004 to 0.012%; Mn: 1.00% or less; S: 0.050% or less; a total of 0.01 to 0.20% of one or both of Sn and Sb; and the remainder: Fe and impurities.