An object of the present invention is to provide a steel sheet and a member that have a high strength, excellent shape uniformity, and excellent delayed fracture resistance and methods for producing the steel sheet and the member.
A steel sheet according to the present invention includes a steel microstructure including, by area, martensite: 20% or more and 100% or less, ferrite: 0% or more and 80% or less, and the balance: 5% or less. A residual stress generated at the transverse center of the steel sheet when the steel sheet is subjected to a V-bending process is 800 MPa or less. A residual stress generated at the transverse end of the steel sheet when the steel sheet is subjected to a V-bending process is 90% or more and 110% or less of the residual stress generated at the transverse center of the steel sheet. The maximum amount of warpage of the steel sheet sheared to a length of 1 m in the longitudinal direction is 15 mm or less.