An aluminum alloy foil for an electrode current collectors has a high post-drying strength after application of an active material while keeping a high electrical conductivity. The aluminum alloy foil includes 0.1 to 1.0 mass % of Fe, 0.01 to 0.5% of Si, and 0.01 to 0.2 mass % of Cu, and the rest includes Al and unavoidable impurities. The aluminum alloy foil after final cold rolling has a tensile strength of 220 MPa or higher, a 0.2% yield strength of 180 MPa or higher, and an electrical conductivity of 58% IACS or higher. The aluminum alloy foil has a tensile strength of 190 MPa or higher and a 0.2% yield strength of 160 MPa or higher after the aluminum alloy foil is heat treated at any of 120° C. for 24 hours, 140° C. for 3 hours, and 160° C. for 15 minutes.