A process includes solution heat treating a nickel based superalloy with greater than about 40% by volume of gamma prime precipitate to dissolve the gamma prime precipitate in the nickel based superalloy; cooling the nickel based superalloy to about 85% of a solution temperature measured on an absolute scale to coarsen the gamma prime precipitate such that a precipitate structure is greater than about 0.7 micron size; and wrought processing the nickel based superalloy at a temperature below a recrystallization temperature of the nickel based superalloy. A material includes a nickel based superalloy with greater than about 40% by volume of gamma prime precipitate in which the precipitate structure is greater than about 0.7 micron size.