Provided is an active energy beam-curable ink capable of preventing ink flow by enhancing the separation resistance of the ink components at high temperatures without impairing the stability against viscosity changes due to high temperatures. The active energy beam-curable ink contains hydrophilic silica with a primary particle diameter of 100 nm or less. It is preferable that a specific surface of the hydrophilic silica be 280 m2/g or less. It is more preferable that the primary particle diameter and the specific surface of the hydrophilic silica be 28 nm or less and 190 m2/g or less, respectively. Moreover, the ink preferably contains a monomer having ethylene oxide units. The number of ethylene oxide units is preferably 6 to 19. The monomer content is preferably 0.02% by mass to 20% by mass with respect to the total mass of the ink.