The present disclosure provides for a formula and process for making elastomeric rubber thin film articles. In particular, the formula and process is a system which produces non-Hevea or Guayule natural rubber latex (GNRL) thin film articles which have a thickness of 30-80 microns (0.03-0.08 mm), and preferably less than 40 microns (0.04 mm). These thin film articles exhibit physical strength properties similar to that of Hevea brazilensis natural rubber latex (NRL). More specifically, the disclosed thin rubber thin film articles exhibit unaged tensile strength of at least 24 MPa (about 3500 psi) and aged tensile strength of at least 19 MPa (about 2800 psi).