A method is provided for the synthesis of a mesoporous lithium transition metal compound, the method comprising the steps of (i) reacting a lithium salt with one or more transition metal salts in the presence of a surfactant, the surfactant being present in an amount sufficient to form a liquid crystal phase in the reaction mixture (ii) heating the reaction mixture so as to form a sol-gel and (iii) removing the surfactant to leave a mesoporous product. The mesoporous product can be an oxide, a phosphate, a borate or a silicate and optionally, an additional phosphate, borate or silicate reagent can be added at step (i). The reaction mixture can comprise an optional chelating agent and preferably, the reaction conditions at steps (i) and (ii) are controlled so as to prevent destabilisation of the liquid crystal phase. The invention is particularly suitable for producing mesoporous lithium cobalt oxide and lithium iron phosphate. The method can be used to synthesise mesoporous lithium cobalt oxide having a specific surface area in excess of 10 m2/g, preferably 15 m2/g or more.