(1) An elastic nonwoven fabric and a fiber product using the elastic nonwoven fabric, the elastic nonwoven fabric containing a crystalline resin composition containing low crystalline polypropylene and high crystalline polypropylene, the low crystalline polypropylene satisfying items (a) and (b) below, and a crystallization temperature (Tc) of the crystalline resin composition measured with a differential scanning calorimeter (DSC) being from 20 to 100° C.: (a) a melting point (Tm-D) being from 0 to 120° C., which is defined as a peak top of a peak observed on the most high temperature side of a melt endothermic curve obtained by maintaining at −10° C. for 5 minutes and increasing in temperature at 10° C. per minute in a nitrogen atmosphere with a differential scanning calorimeter (DSC); and (b) a stereoregularity index ([mm]) being from 50 to 90% by mol; (2) an elastic nonwoven fabric and a fiber product using the elastic nonwoven fabric, the elastic nonwoven fabric being produced by using a crystalline resin composition containing low crystalline polypropylene satisfying items (c) to (h) below, and a releasing agent: (c) [mmmm]=20 to 60% by mol; (d) [rrrr]/(1−[mmmm])≦0.1; (e) [rmrm]>2.5% by mol; (f) [mm]×[rr]/[mr]2≦2.0; (g) mass average molecular weight (Mw)=10,000 to 200,000; and (h) molecular weight distribution (Mw/Mn)