High modulus turbine shafts and high modulus cylindrical articles are described as are the process parameters for producing these shafts and cylindrical articles. The shafts/articles have a high Young's modulus as a result of having high modulus crystal texture along the longitudinal axis of the shaft/article. The shafts are produced from directionally solidified seeded single crystal cylinders that are axisymmetrically hot worked before a limited recrystallization process is carried out at a temperature below the recrystallization temperature of the alloy. The disclosed process produces an intense singular texture and results in shaft or cylindrical article with a Young's modulus that is at least 40% greater than that of conventional nickel or iron alloys or conventional steels.