To provide a glass laminate of which an increase of the peel strength between a glass substrate and a silicone resin layer is suppressed even after a high temperature heat treatment, and from which the glass substrate can readily be separated. A glass laminate comprising a support substrate, a silicone resin layer and a glass substrate in this order, with a peel strength at the interface between the support substrate and the silicon resin layer higher than the peel strength at the interface between the silicone resin layer and the glass substrate, wherein a silicone resin in the silicone resin layer is a cured product obtained by reacting an alkenyl-group containing organopolysiloxane (A) and a hydrogen polysiloxane (B) having a hydrosilyl group, and the mixing molar ratio of the hydrosilyl groups in the hydrogen polysiloxane (B) to the alkenyl groups in the alkenyl group-containing organopolysiloxane (A) (that is, number of mols of hydrosilyl groups/number of mols of alkenyl groups) is from 0.15/1 to 0.65/1.