A polymer composition adapted for use in injection stretch blow molding may include a metallocene random propylene-based copolymer in the absence of a clarifier. The metallocene random propylene-based copolymer may exhibit a melting point of from 105° C. to less than 175° C., a recrystallization temperature ranging from 85° C. to 100° C. as measured by DSC, a microtacticity ranging from 89% to 99%, a molecular weight (Mw) ranging from 170,000 to 210,000, and a melt flow rate of from about 1 dg/min. to about 40 dg/min. A method of forming an injection stretch blow molded (ISBM) article may include providing the metallocene random propylene-based copolymer, injection molding the metallocene random propylene-based copolymer in the absence of a clarifier into a preform, and stretch-blowing the preform into an article.