A high-strength galvanized steel sheet includes a steel sheet having a steel composition having a specific component composition, a steel structure containing martensite and bainite at more than or equal to 70% (including 100%), ferrite at less than 20% (including 0%), and retained austenite at less than 5% (including 0%) in terms of area ratio, the amount of diffusible hydrogen in steel being less than or equal to 0.20 mass ppm; and a galvanizing layer provided on a surface of the steel sheet, having a content amount of Fe of 8 to 15% in mass %, and having an coating weight per one surface of 20 to 120 g/m2, wherein the amount of Mn oxides contained in the galvanizing layer is less than or equal to 0.050 g/m2, and a tensile strength is more than or equal to 1100 MPa and a yield ratio is more than or equal to 0.85.