The present invention provides a method for the manufacture of transition metal oxide fine particles, the method comprising the steps of: heating a strong-alkaline aqueous solution while stirring same; adding to and dissolving in the heated strong-alkaline aqueous solution a transition metal oxide; adding a strong-acid aqueous solution to the strong alkaline aqueous solution in which the transition metal oxide is dissolved, while stirring same, thereby re-dissolving a solid generated at the interface between the strong-alkaline aqueous solution and the strong-acid aqueous solution; adjusting the pH of the mixed aqueous solution resulting from mixing the strong-alkaline aqueous solution and the strong acid aqueous solution, through adjustment of the adding rate and amount of the strong-acid aqueous solution, to precipitate transition metal oxide fine particles; and separating the transition metal oxide fine particles from the mixed aqueous solution and sequentially washing, drying, and thermally treating the separated transition metal oxide fine particles.