The present invention relates to a non-grain-oriented electrical steel sheet which is excellent in high-frequency iron loss, and a manufacturing method thereof.
A non-grain-oriented electrical steel sheet according to an exemplary embodiment of the present invention includes 2.5 to 3.8 wt % of Si, 0.5 to 2.5 wt % of Al, 0.2 to 4.5 wt % of Mn, 0.0005 to 0.02 wt % of As, 0.0005 to 0.01 wt % of Bi, the balance Fe, and inevitable impurities, and satisfies the following [Equation 1]. 0.3≤[surface fine crystal grain diameter]×[fine grain formation thickness]×([As]/[Bi])≤5.0  [Equation 1] In Equation 1, [surface fine crystal grain diameter] means an average particle diameter (μm) of fine crystal grains in an electrode surface layer of an electrical steel sheet, [fine grain formation thickness] means a thickness (mm) of an electrode surface layer in which fine crystal grains are formed, and [As] and [Bi] mean a composition (wt %) of As and a composition (wt %) of Bi, respectively.