In a process for manufacturing glass, a mixture of solid glass-forming materials (18) may be melted by application of heat from one or more submerged combustion burners (34) to produce a volume of unrefined molten glass comprising, by volume, 20% to 40% gas bubbles. A refining agent may be introduced into the unrefined molten glass to promote gas bubble removal from the molten glass. The unrefined molten glass including the refining agent may be heated at a temperature in the range of 1200° C. to 1500° C. to produce a volume of refined molten glass. The refined molten glass may comprise, by volume, fewer gas bubbles than the unrefined molten glass. A colorant material may be introduced into the refined molten glass to produce a volume of molten glass having a final desired color.