This invention relates to a method of producing a paste-type electrode for a lead storage battery which comprises packing into an active material support a paste prepared by kneading a lead oxide having a conversion ratio to red lead (Pb.sub.3 O.sub.4) of 90% or less or a mixture of this lead oxide powder with water and sulfuric acid as the principal components. Because this lead oxide contains red lead less than 90%, red lead formed on the surface of this oxide and lead oxide (PbO) formed in the particle core are directly bonded. This enhances the bonding power between the active materials. The paste-type electrode prepared by this method provides high adhesion of the paste to the active material support and high bonding power between the active materials. Therefore, both improvements in life and in efficiency of formation charge can be attained.