An oxide superconductor article is provided having an oxide superconductor film having a thickness of greater than 0.5 microns disposed on a substrate, said article having a transport critical current density (Jc) of greater than or equal to about 105 A/cm2 at 77 K, zero field. The oxide superconductor film is characterized by high Jc and high volume percent of c-axis epitaxial oxide grains, even with thicknesses of up to 1 micron. The oxide superconductor article is prepared by providing a metal oxyfluoride film, said metal oxyfluoride film comprising the constituent metallic elements of an oxide superconductor in substantially stoichiometric proportions; and converting the metal oxyfluoride into the oxide superconductor at a rate of conversion selected by adjusting a reaction parameter selected from the group consisting of temperature, PH2O, PO2, and time and combinations thereof, such that an oxide superconductor film having a transport critical current density of greater than or equal to about 105 A/cm2 at 77 K, zero field is obtained.