Steel strips and methods for producing steel strips are provided. In an illustrated embodiment, a method includes continuously casting molten low carbon steel into a strip of no more than 5 mm thickness having austenite grains that are coarse grains of 100-300 micron width; and providing desired yield strength in the cast strip by cooling the strip to transform the austenite grains to ferrite in a temperature range between 850° C. and 400° C. at a selected cooling rate of at least 0.01° C./sec to produce a microstructure that provides a strip having a yield strength of at least 200 MPa. The low carbon steel produced desired microstructure.