A tin-plated steel sheet includes a plating layer containing tin on at least one surface of a steel sheet, and a chemical conversion coating containing P and tin on the plating layer is provided. In the steel sheet, a coated amount of the chemical conversion coating per surface is 1.0 to 50 mg/m2 in terms of P, an atomic ratio Sn/P obtained from the intensity of a P2p peak and that of a Sn3d peak is 1.0 to 1.5, the intensities being measured at the surface using an x-ray photoelectron spectroscopic method, and an atomic ratio O/P obtained from the intensity of the P2p peak and that of an O1s peak is 4.0 to 9.0. The phosphoric acid-based chemical conversion coating of the tin-plated steel sheet can suppress degradation in performance, which is caused by the growth of a tin oxide layer on the surface, instead of a conventional chromate coating.