A process for repairing cracks in a workpiece, such as a turbine engine component, comprises the steps of: providing a workpiece having a crack to be repaired; applying a nickel or cobalt base alloy material to a root of the crack in an amount sufficient to fill a portion of the crack; subjecting the workpiece with the nickel or cobalt base alloy material to a first heat treatment at a temperature in the range of from about 1950 to 2300° F. for a time period in the range of from about 5.0 to 30 minutes; applying a weld material to the crack; and subjecting the workpiece with the weld material to a second heat treatment.